Effects Of Aggregate Sizes On The Concrete Strength
In the sense that the materials involved in this project were capital intensive more especially cement, so in carrying out the work one must hsve to be careful in the selection and collection of materials to be used in the casting of the concrete.
The materials used are coarse aggregate (granite) fine aggregate (sand). The coarse aggregates used in this work were collected from ishiagu while the fine aggregate was collected in front of the carpentry’s workshop on the campus.
The test conform to the standard method test, the ratio used was 1:2:4 and the method adopted was batching by weight, from the mix ratio the relative weight for each material to be used for concrete cube cast was 36, these cubes were tested for compressive strength of 7, 14 and 28 days.
The results of tests involved in the work and that of compressive strength tests were calculated and tabulated as shown in the final tabulation of results.
With the above information, I now recommend and therefore conclude.
NOTE: Preview the following Table of Content before you download the full content. WYSIWYG – What You See Is What You Get.
Title page
Latter of transmittal
Approval page
Dedication
Acknowledgement
Abstract
Table of contents
CHAPTER ONE
1.1 The project objectives
CHAPTER TWO
2.1 Materials for concrete
2.2 Aggregates introduction
2.2.1 Fine Aggregate/Sand
2.2.2 Coarse Aggregate/Granite
CHAPTER THREE
3.0 Mixing of the concrete
CHAPTER FOUR
4.0 Preparation for placing and compaction
CHAPTER FIVE
5.0 Curing
CHAPTER SIX
6.0 Testing of hardened concrete and tabulation of results
CHAPTER SEVEN
7.0 Conclusions and recommendation
Bibliography.
This “Effects Of Aggregate Sizes On The Concrete Strength” file contains 7 Chapters, 29 Pages and 3,088 Words.
The author of Effects Of Aggregate Sizes On The Concrete Strength is written at the front page of the downloaded file.
To download this Effects Of Aggregate Sizes On The Concrete Strength full file, click on “Download File” on top of this page and follow the next.